Pengaruh Transformasi Ketahanan Mekanik Akibat Proses Quenching terhadap Material Pipa Minyak dan Gas pada Pengujian Bending: Penelitian

Alexander Sebayang; Fida Hanum; Muhammad Ariyon; Fitriati; Ira Herawati; Efrata Tarigan; Idhamkamil; Liwat Tarigan

doi:10.31004/jerkin.v2i4.1610

Authors

Alexander Sebayang Polytechnic of Medan
Fida Hanum Islamic University Riau
Muhammad Ariyon Polytechnic of Medan
Fitriati Polytechnic of Medan
Ira Herawati Islamic University Riau
Efrata Tarigan Islamic University Riau
Idhamkamil Polytechnic of Medan
Liwat Tarigan Polytechnic of Medan

DOI:

https://doi.org/10.31004/jerkin.v2i4.1610

Keywords:

Kekuatan Bending, Root Bend, Face Bend, Struktur Martensit, Quenching

Abstract

Pada perkembangan dan kemajuan dalam dunia minyak dan gas yang semakin pesat, pemilihan material dan penyambungan pada material tidak bisa dilepaskan. Dengan demikian, pemilihan material dan metode pengelasan pipa penyalur minyak dan gas bumi harus mengacu pada standar yang ada. Proses perlakuan panas quenching merupakan salah satu metode yang efektif untuk meningkatkan sifat mekanik material logam, khususnya pada kekuatan bending. Penelitian ini bertujuan untuk membandingkan kekuatan bending material dalam kondisi raw material dan setelah melalui proses quenching. Pengujian dilakukan pada dua jenis pembebanan, yaitu root bend dan face bend. Hasil pengujian menunjukkan bahwa material yang telah mengalami proses quenching memiliki nilai kekuatan bending yang lebih tinggi, masing-masing sebesar 1377,41 MPa untuk root bend dan 1339,43 MPa untuk face bend, dibandingkan dengan raw material yang memiliki kekuatan 1110,63 MPa dan 1141,67 MPa. Peningkatan ini menandakan bahwa proses quenching mampu meningkatkan ketahanan material terhadap beban lentur, baik pada sisi akar maupun permukaan spesimen. Fenomena ini diduga disebabkan oleh terbentuknya struktur martensit yang lebih keras dan padat akibat pendinginan cepat selama proses quenching. Temuan ini sejalan dengan berbagai literatur ilmiah yang menunjukkan bahwa transformasi mikrostruktur menjadi martensit berkontribusi signifikan terhadap peningkatan kekuatan mekanik material.

References

Wiryosumarto H dan Toshie Okumura, “Teknologi Pengelasan Logam, PT. Pradnya Paramita, Jakarta,” 1979.

F. Purba, M. F. I., Fathier, A., “Pengaruh Variasi Temperatur PWHT dan Tanpa PWHT Terhadap Sifat Kekerasan Baja ASTM A106 Grade B Pada Proses Pengelasan SMAW. Journal of Welding Technology. Volume 2, No. 1.,” 2020.

ASTM. A106-99, “Standard Specification for Seamless Carbon Steel Pipe for High Temperature Service.,” 1999.

D. P. B. Prayitno, D., Hutagalung, H. D., & Aji, “Pengaruh kuat arus listrik pengelasan terhadap kekerasan lapisan lasan pada baja astm a316, 7590.,” 2018.

J. Ahmed, K., Krishnan, “Post-Weld Heat Treatment-Case Studies, BARC Newsletter, Available,” 2002.

ASME, Qualification Standard for Welding and Brazing Procedures, Welders, Brazers, and Welding and Brazing Operators, Sec. IX, American Society of Mechanical Engineering, New York. 2020.

ASM Handbook, “Heat Treating, Vol. 4, American Soeciety for Metal, International.,” 1991.

ASM Handbook, “Welding, Brazing, and Soldering, Vol.6, American Soeciety for Metal, Ohio.,” 1993.

R. S. Funderburk, “Welding Innovation, Vol. XV, Key Concepts in Welding Engineering.,” 1998.

W. D. Callister Jr., “Fundamentals of Material Science and Engineering, Edisi ke-4, Erlangga, Jakarta,” 2001.

P. D. Wirarchi, “Analisa Pengaruh Multiple Repair Welding Pada Material Properties Weld Joint Material Pipa ASTM A106 Gr.B Sch 80, Tugas Akhir Teknik Mesin, ITS, Surabaya.,” 2007.

Basori, “‘Pengaruh Media Quenching terhadap Kekerasan dan Struktur Mikro Paska Hardfacing.’ Jurnal Kajian Teknik Mesin. Vol. 3.2: hal. 66-72.,” 2018.

Bahtiar, Muh. Iqbal dan Supramono., “‘Pengaruh Media Pendingin Minyak Pelumas Sae 40 Pada Proses Quenching dan Tempering Terhadap Ketangguhan Baja Karbon Rendah’. Jurnal Mekanikal Vol. 5 No. 1: Januari 2014, pp: 455- 463.,” 2014.

M. Andreansyah, R. D. Anjani, and V. Naubnome, “Pengaruh Proses Heat Treatment ( Quenching dan Tempering ) Terhadap Kekerasan dan Struktur Mikro Baja Karbon Menengah,” vol. IX, no. 1, pp. 7864–7872, 2024.

M. I. S. Pilisi, I. Suroso, and N. Utami, “Pengaruh quenching terhadap uji kekerasan dan uji impact disc brake cessna grand caravan 208b,” SINTEK J. J. Ilm. Tek. Mesin, vol. 16, no. 1, p. 61, 2022, doi: 10.24853/sintek.16.1.61-67.